Effect of vanadium on failure peculiarities of high strength steel wire. / Baraz, V. R.; Sokolov, A. A.; Ishina, E. A. и др.
в: Metallovedenie i Termicheskaya Obrabotka Metallov, № 9, 1991, стр. 11-13.

Результаты исследований: Вклад в журнал › Статья › Рецензирование

Harvard

Baraz, VR, Sokolov, AA, Ishina, EA & Glomazova, TV 1991, 'Effect of vanadium on failure peculiarities of high strength steel wire', Metallovedenie i Termicheskaya Obrabotka Metallov, № 9, стр. 11-13.

APA

Baraz, V. R., Sokolov, A. A., Ishina, E. A., & Glomazova, T. V. (1991). Effect of vanadium on failure peculiarities of high strength steel wire. Metallovedenie i Termicheskaya Obrabotka Metallov, (9), 11-13.

Vancouver

Baraz VR, Sokolov AA, Ishina EA, Glomazova TV. Effect of vanadium on failure peculiarities of high strength steel wire. Metallovedenie i Termicheskaya Obrabotka Metallov. 1991;(9):11-13.

Author

Baraz, V. R. ; Sokolov, A. A. ; Ishina, E. A. и др. / Effect of vanadium on failure peculiarities of high strength steel wire. в: Metallovedenie i Termicheskaya Obrabotka Metallov. 1991 ; № 9. стр. 11-13.

BibTeX

@article{3fb5a9bd9dac4835bc2eafc264b58cc2,
title = "Effect of vanadium on failure peculiarities of high strength steel wire",
abstract = "The possibility to increase the properties of high strength carbon steel wire (0.7% C) by vanadium microalloying (0.1%) was studied. Mechanical properties and density were measured on steels with and without vanadium. It was established that microalloying with V diminish the tendency to splitting fracture after moderate deformations. After ε>80% the tendency to splitting can remain. The positive effect of microalloying is caused by the delay of the process of cementite disintegration under drawing of heat - treated wires and decrease of the deformation aging process, that affects the intensity of crack propagations under deformation.",
author = "Baraz, {V. R.} and Sokolov, {A. A.} and Ishina, {E. A.} and Glomazova, {T. V.}",
year = "1991",
language = "Русский",
pages = "11--13",
journal = "Metallovedenie i Termicheskaya Obrabotka Metallov",
issn = "0026-0819",
publisher = "Folium Publishing Company",
number = "9",

}

RIS

TY - JOUR

T1 - Effect of vanadium on failure peculiarities of high strength steel wire

AU - Baraz, V. R.

AU - Sokolov, A. A.

AU - Ishina, E. A.

AU - Glomazova, T. V.

PY - 1991

Y1 - 1991

N2 - The possibility to increase the properties of high strength carbon steel wire (0.7% C) by vanadium microalloying (0.1%) was studied. Mechanical properties and density were measured on steels with and without vanadium. It was established that microalloying with V diminish the tendency to splitting fracture after moderate deformations. After ε>80% the tendency to splitting can remain. The positive effect of microalloying is caused by the delay of the process of cementite disintegration under drawing of heat - treated wires and decrease of the deformation aging process, that affects the intensity of crack propagations under deformation.

AB - The possibility to increase the properties of high strength carbon steel wire (0.7% C) by vanadium microalloying (0.1%) was studied. Mechanical properties and density were measured on steels with and without vanadium. It was established that microalloying with V diminish the tendency to splitting fracture after moderate deformations. After ε>80% the tendency to splitting can remain. The positive effect of microalloying is caused by the delay of the process of cementite disintegration under drawing of heat - treated wires and decrease of the deformation aging process, that affects the intensity of crack propagations under deformation.

UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=0026224759

M3 - Статья

SP - 11

EP - 13

JO - Metallovedenie i Termicheskaya Obrabotka Metallov

JF - Metallovedenie i Termicheskaya Obrabotka Metallov

SN - 0026-0819

IS - 9

ER -

ID: 55014205