T1 - Effect of vanadium on failure peculiarities of high strength steel wire
AU - Baraz, V. R.
AU - Sokolov, A. A.
AU - Ishina, E. A.
AU - Glomazova, T. V.
PY - 1991
Y1 - 1991
N2 - The possibility to increase the properties of high strength carbon steel wire (0.7% C) by vanadium microalloying (0.1%) was studied. Mechanical properties and density were measured on steels with and without vanadium. It was established that microalloying with V diminish the tendency to splitting fracture after moderate deformations. After ε>80% the tendency to splitting can remain. The positive effect of microalloying is caused by the delay of the process of cementite disintegration under drawing of heat - treated wires and decrease of the deformation aging process, that affects the intensity of crack propagations under deformation.
AB - The possibility to increase the properties of high strength carbon steel wire (0.7% C) by vanadium microalloying (0.1%) was studied. Mechanical properties and density were measured on steels with and without vanadium. It was established that microalloying with V diminish the tendency to splitting fracture after moderate deformations. After ε>80% the tendency to splitting can remain. The positive effect of microalloying is caused by the delay of the process of cementite disintegration under drawing of heat - treated wires and decrease of the deformation aging process, that affects the intensity of crack propagations under deformation.
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=0026224759
M3 - Статья
SP - 11
EP - 13
JO - Metallovedenie i Termicheskaya Obrabotka Metallov
JF - Metallovedenie i Termicheskaya Obrabotka Metallov
SN - 0026-0819
IS - 9
ER -
ID: 55014205