TY - JOUR
T1 - Impact of Ln cation on the oxygen ion conductivity of Ln14W4O33 (Ln = Nd, Sm, Gd, Dy, Ho, Er, Tm, Yb) tungstates
AU - Shlyakhtina, Anna
AU - Lyskov, Nikolay
AU - Baldin, Egor
AU - Stolbov, Dmitriy
AU - Kolbanev, Igor
AU - Shatov, Alexander
AU - Kasyanova, Anna
AU - Medvedev, Dmitriy
N1 - The work was supported partially by the subsidy from the Ministry of Education and Science allocated by the FRC CP RAS for the implementation of the state assignment (No. 122040500071-0 and in accordance with the state task for FRC PCP and MC RAS, state registration No. АААА-А19-119061890019-5.
PY - 2024
Y1 - 2024
N2 - Tungstates Ln14W4O33 (Ln = Nd, Sm, Gd, Dy, Ho, Er, Tm, Yb) with a pseudorhombohedral structure have been synthesized by a short high temperature annealing (1450–1600 °С) from mechanically activated mixtures of oxides. The resulting ceramics were studied by X-ray diffraction, Raman and SEM analyses. The conductivity of ceramics was measured by the 4-probe direct current method in dry and wet atmospheres (oxidizing and reducing) and by impedance spectroscopy. In order to estimate the ionic and electronic contributions to the total conductivity, the dependences of the conductivity on the oxygen partial pressure (pO2) were determined at temperatures between 700 and 900 °C. Ln14W4O33 (Ln = Nd, Sm, Gd) tungstates have a wide electrolytic range (10−15–1 atm) above 700 °C. It should be noted that under oxidizing conditions the contribution of hole conductivity is absent in these compounds. Among the pseudorhombohedral phases of Ln14W4O33 (Ln = Nd, Sm, Gd), Nd14W4O33 exhibits the highest oxygen-ion conductivity (4 × 10−4 S/cm at 700 °C). The electrolytic domain of the second half of the REE Ln14W4O33 (Ln = Dy, Ho, Er, Tm, Yb) series becomes narrower (10−10–10−5 atm) and at the same time has a slight slope indicating the presence of impurity electronic charge carriers. Investigations in a reducing atmosphere confirmed that the reduction tendency increases with decreasing lanthanide ionic radius in the Ln14W4O33 tungsten series. The variations of the total conductivity in the series of pseudorhombohedral phases Ln14W4O33 (Ln = Dy, Ho, Er, Tm, Yb) are associated with local changes in the short-range order structure (Raman spectroscopy). When Ln14W4O33 (Ln = Nd, Gd) is exposed to water at room temperature for an extended period of time, the total conductivity decreases due to the diffusion of the Nd and Gd cations into the water.
AB - Tungstates Ln14W4O33 (Ln = Nd, Sm, Gd, Dy, Ho, Er, Tm, Yb) with a pseudorhombohedral structure have been synthesized by a short high temperature annealing (1450–1600 °С) from mechanically activated mixtures of oxides. The resulting ceramics were studied by X-ray diffraction, Raman and SEM analyses. The conductivity of ceramics was measured by the 4-probe direct current method in dry and wet atmospheres (oxidizing and reducing) and by impedance spectroscopy. In order to estimate the ionic and electronic contributions to the total conductivity, the dependences of the conductivity on the oxygen partial pressure (pO2) were determined at temperatures between 700 and 900 °C. Ln14W4O33 (Ln = Nd, Sm, Gd) tungstates have a wide electrolytic range (10−15–1 atm) above 700 °C. It should be noted that under oxidizing conditions the contribution of hole conductivity is absent in these compounds. Among the pseudorhombohedral phases of Ln14W4O33 (Ln = Nd, Sm, Gd), Nd14W4O33 exhibits the highest oxygen-ion conductivity (4 × 10−4 S/cm at 700 °C). The electrolytic domain of the second half of the REE Ln14W4O33 (Ln = Dy, Ho, Er, Tm, Yb) series becomes narrower (10−10–10−5 atm) and at the same time has a slight slope indicating the presence of impurity electronic charge carriers. Investigations in a reducing atmosphere confirmed that the reduction tendency increases with decreasing lanthanide ionic radius in the Ln14W4O33 tungsten series. The variations of the total conductivity in the series of pseudorhombohedral phases Ln14W4O33 (Ln = Dy, Ho, Er, Tm, Yb) are associated with local changes in the short-range order structure (Raman spectroscopy). When Ln14W4O33 (Ln = Nd, Gd) is exposed to water at room temperature for an extended period of time, the total conductivity decreases due to the diffusion of the Nd and Gd cations into the water.
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=85175236711
UR - https://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=tsmetrics&SrcApp=tsm_test&DestApp=WOS_CPL&DestLinkType=FullRecord&KeyUT=001133386100001
U2 - 10.1016/j.ceramint.2023.10.149
DO - 10.1016/j.ceramint.2023.10.149
M3 - Article
VL - 50
SP - 704
EP - 713
JO - Ceramics International
JF - Ceramics International
SN - 0272-8842
IS - 1, Part A
ER -