TY - JOUR
T1 - Detailed investigations for mechanical and gamma-ray attenuation characteristics of B2O3-ZnO-BaO-TiO2 glasses doped with PbO
AU - Sayyed, M.
AU - Almuqrin, Aljawhara
AU - Mahmoud, K.
PY - 2024
Y1 - 2024
N2 - The effect of PbO addition with different concentrations on four synthesized zinc titanium borate glasses with the chemical formula xPbO-(75-x) B2O3-10ZnO-10BaO-5TiO2 (x = 30, 35, 40, and 45 mol%) was explored in this study. The partial PbO substitution for B2O3 increases the fabricated glasses' density by ≈ 20% from 5.31 to 6.37 g/cm3, respectively, with raising the PbO concentrations between 30 and 45 mol.%, respectively. Besides, the substitution mentioned above enhances the gamma-ray attenuation properties where the linear attenuation coefficient increased between 69.911 and 102.245 cm−1 (at 0.033 MeV), 0.341–0.415 cm−1 (at 1 MeV), and 0.200–0.262 cm−1 (at 10 MeV), increasing the PbO concentration between 30 and 45 mol.%, respectively. Simultaneously, increases in the PbO concentration within the fabricated glasses decrease the lead's equivalent thickness between 3.82 and 2.61 cm (at 0.033 MeV), 2.35–1.93 cm (at 1 MeV), and 2.81–2.14 cm (at 10 MeV). In contrast, substituting PbO for B2O3 compounds diminishes the fabricated glasses' mechanical properties, where the microhardness decreased by 13.5 % from 4.24 to 3.67 GPa. The lead equivalent thickness (Deq) values at 0.66 MeV were found equal to 2.410, 2.232, 2.078, and 1.945 cm, and at 1.112 MeV, these values were found equal to 2.222, 2.081, 1.956, and 1.829 cm for G1, G2, G3, and G4, respectively. © 2024 The Authors
AB - The effect of PbO addition with different concentrations on four synthesized zinc titanium borate glasses with the chemical formula xPbO-(75-x) B2O3-10ZnO-10BaO-5TiO2 (x = 30, 35, 40, and 45 mol%) was explored in this study. The partial PbO substitution for B2O3 increases the fabricated glasses' density by ≈ 20% from 5.31 to 6.37 g/cm3, respectively, with raising the PbO concentrations between 30 and 45 mol.%, respectively. Besides, the substitution mentioned above enhances the gamma-ray attenuation properties where the linear attenuation coefficient increased between 69.911 and 102.245 cm−1 (at 0.033 MeV), 0.341–0.415 cm−1 (at 1 MeV), and 0.200–0.262 cm−1 (at 10 MeV), increasing the PbO concentration between 30 and 45 mol.%, respectively. Simultaneously, increases in the PbO concentration within the fabricated glasses decrease the lead's equivalent thickness between 3.82 and 2.61 cm (at 0.033 MeV), 2.35–1.93 cm (at 1 MeV), and 2.81–2.14 cm (at 10 MeV). In contrast, substituting PbO for B2O3 compounds diminishes the fabricated glasses' mechanical properties, where the microhardness decreased by 13.5 % from 4.24 to 3.67 GPa. The lead equivalent thickness (Deq) values at 0.66 MeV were found equal to 2.410, 2.232, 2.078, and 1.945 cm, and at 1.112 MeV, these values were found equal to 2.222, 2.081, 1.956, and 1.829 cm for G1, G2, G3, and G4, respectively. © 2024 The Authors
UR - http://www.scopus.com/inward/record.url?partnerID=8YFLogxK&scp=85189935591
UR - https://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=tsmetrics&SrcApp=tsm_test&DestApp=WOS_CPL&DestLinkType=FullRecord&KeyUT=001230352500001
U2 - 10.1016/j.jmrt.2024.04.035
DO - 10.1016/j.jmrt.2024.04.035
M3 - Article
VL - 30
SP - 3011
EP - 3020
JO - Journal of Materials Research and Technology
JF - Journal of Materials Research and Technology
SN - 2238-7854
ER -
ID: 55702364