In this study, 2-line ferrihydrite (2L Fh) nanoparticles (NPles)were synthesized by radiation-chemical method from an alcoholic solution of iron (III) nitrate for the first time. The X-ray diffraction analysis confirmed that the synthetic powder exhibited the characteristic pattern of 2L Fh NPles. DSC-TG analysis conducted in air atmosphere further verified the formation of 2L Fh. SEM analysis showed the presence of mesoporous plate-like structures in the 2L Fh powder, consisting of aggregates of NPs with an average size of approximately 20 nm. The absence of impurity peaks on the X-ray diffractograms and energy dispersion spectra (EDX) confirmed the chemical purity of the produced 2L Fh NPles. Additionally, the XPS method detected the presence of nitrogen and carbon adsorbed to the developed surface of the 2L Fh plates. 2L Fh NPles, when dried in air at a temperature of 50 °C, rapidly dissolved in water. 2L Fh NPles alcohol suspensions were stabilized using surfactants polyethylenimine (PEI) and acetylacetone (AcAs). 2L Fh NPles showed good photocatalytic properties when irradiated with ultraviolet light of methyl violet (MV) dye. These 2L Fh NPles, synthesized using an environmentally friendly radiation-chemical method, have immense potential for applications in biomedicine and photocatalysis.