The homogeneity range limit for the La2-xCaxNi1-yFeyO4+δ (x=0.5 y=0.2, 0.3; x=0.6, y=0.4, 0.42) solid solutions at 1100° C in air has been established. The temperature dependences of oxygen non-stoichiometry were obtained for La1.5Ca0.5Ni0.7Fe0.3O4+δ (δ=0.08, T=25 °C) and La1.4Ca0.6Ni0.6Fe0.4O4+δ (δ=0.06, T=25 °C). Total conductivity of La2-xCaxNi1-yFeyO4+δ increases with temperature and decreases with iron doping. The activation energy of conductivity varies in the range of 12-17.4 kJ/mol. The polarization resistance of the La1.4Ca0.6Ni0.6Fe0.4O4+δ/Ce0.8Sm0.2O2-δ symmetric cell is equal to 4.62 Ω cm2 at 800 °С.
Translated title of the contributionPHYSICOCHEMICAL PROPERTIES AND ELECTROCHEMICAL IMPEDANCE OF PHASES FORMED IN THE LA2-XCAXNI1-YFEYO4+δ SYSTEM: book chapter
Original languageRussian
Title of host publicationАКТУАЛЬНЫЕ ПРОБЛЕМЫ РАЗВИТИЯ ЕСТЕСТВЕННЫХ НАУК: сборник статей участников XXIV Областного конкурса научно-исследовательских работ «Научный Олимп» по направлению «Естественные науки»
Subtitle of host publicationсборник статей
Place of PublicationЕкатеринбург
PublisherФедеральное государственное автономное образовательное учреждение высшего профессионального образования "Уральский федеральный университет им. первого Президента России Б.Н. Ельцина"
Pages140-145
Number of pages6
ISBN (Print)978-5-91256-538-0
Publication statusPublished - 2021

    GRNTI

  • 43.01.00

ID: 29227843