The result of process modeling of zirconium reduction from oxide using thermal analysis is congruent stable intermetallic compound Al3Zr formation. This process occurs through intermediate stage of zirconium monoxide formation.
Translated title of the contributionThermal Analysis Usage for Process Modelling of Alumino-Thermic Zirconium Reduction from Oxide